产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 熔体流动速率 | 220℃ 10kg | ISO-1133 | 23 | g/10min |
| 比重 | 23℃ | ASTM D-792 | 1.05 | |
| 模塑收缩率 | | ASTM D-955 | 0.4-0.6 | % |
| 体积阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm.cm |
| 阻燃性 | | UL-94 | HB | |
| 吸水性 | 23℃×24hrs | ASTM D-570 | 0.3 | % |
| 表面阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm |
| 机械性能 | 拉伸断裂伸长率 | 23℃ | ASTM D-638 | 35 | % |
| 弯曲模量 | 23℃ | ASTM D-790 | 25000(2450) | kg/cm2(MPa) |
| IZOD冲击强度 | 12.7×62.5×12.7mm | 0℃ | ASTM D-256 | 11(108) | kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm | 0℃ | ASTM D-256 | 16(157) | kg.cm/cm(J/m) |
| IZOD冲击强度 | 12.7×62.5×12.7mm | 23℃ | ASTM D-256 | 19(186) | kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm | 23℃ | ASTM D-256 | 20(196) | kg.cm/cm(J/m) |
| 洛氏硬度 | | ASTM D-785 | 115 | R |
| 弯曲强度 | 23℃(strainrate:3%) | ASTM D-790 | 770(76) | kg/cm2(MPa) |
| IZOD冲击强度 | 12.7×62.5×12.7mm | -30℃ | ASTM D-256 | 8(78) | kg.cm/cm(J/m) |
| 12.7×62.5×3.2mm | -30℃ | ASTM D-256 | 12(118) | kg.cm/cm(J/m) |
| 拉伸强度 | 23℃(strainrate:5%) | ASTM D-638 | 510(50) | kg/cm2(MPa) |
| 电气性能 | 绝缘强度 | Short time | ASTM D-194 | 23 | KV/mm |
| 电力因数 | 1000Hz | ASTM D-150 | 6.1×10-3 | |
| 介电常数 | 1000Hz | ASTM D-150 | 3.1 | |
| 热性能 | 热传导性能 | | ASTM C177 | 0.15 | W/K.m |
| 线性膨胀系数 | | ASTM D-696 | 7.1×10-5 | mm/mm℃ |
| 热变形温度 | 127×12.7×12.7mm | 18.56kg/cm2 | ASTM D-648 | 92 | ℃ |
| 127×12.7×6.4mm | 18.56kg/cm2 | ASTM D-648 | 87 | ℃ |
| 格级别： | 高抗冲级 | 外观颜色： | --- |
| 用途概述： | --- |
| 备注说明： | --- |
②原料技术数据| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | 23℃ | ASTM D-792 | 1.05 | --- |
| 吸水性 | 23℃×24hrs | ASTM D-570 | 0.3 | % |
| 熔体流动速率 | 220℃ 10kg | ISO-1133 | 23 | g/10min |
| 模塑收缩率 | --- | ASTM D-955 | 0.4-0.6 | % |
| 表面阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm |
| 体积阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm.cm |
| 阻燃性 | --- | UL-94 | HB | --- |
| 机械性能 | | IZOD冲击强度 | 12.7×62.5×12.7mm | | 12.7×62.5×3.2mm |
| | | | | kg.cm/cm(J/m) | | kg.cm/cm(J/m) |
|
| IZOD冲击强度 | 12.7×62.5×12.7mm | | 12.7×62.5×3.2mm |
| | | | | kg.cm/cm(J/m) | | kg.cm/cm(J/m) |
|
| IZOD冲击强度 | 12.7×62.5×12.7mm | | 12.7×62.5×3.2mm |
| | | | | kg.cm/cm(J/m) | | kg.cm/cm(J/m) |
|
| 洛氏硬度 | --- | ASTM D-785 | 115 | R |
| 拉伸强度 | 23℃(strainrate:5%) | ASTM D-638 | 510(50) | kg/cm2(MPa) |
| 拉伸断裂伸长率 | 23℃ | ASTM D-638 | 35 | % |
| 弯曲强度 | 23℃(strainrate:3%) | ASTM D-790 | 770(76) | kg/cm2(MPa) |
| 弯曲模量 | 23℃ | ASTM D-790 | 25000(2450) | kg/cm2(MPa) |
| 电气性能 | 绝缘强度 | Short time | ASTM D-194 | 23 | KV/mm |
| 介电常数 | 1000Hz | ASTM D-150 | 3.1 | --- |
| 电力因数 | 1000Hz | ASTM D-150 | 6.1×10-3 | --- |
| 热 性 能 | 热传导性能 | --- | ASTM C177 | 0.15 | W/K.m |
| 热变形温度 | 127×12.7×12.7mm | | 127×12.7×6.4mm |
| | | | |
| 线性膨胀系数 | --- | ASTM D-696 | 7.1×10-5 | mm/mm℃ |
尊敬的客户本公司长供功能性ＡＢＳ（防火，防静电，耐候级，耐环境开裂，耐磨级，抗菌级等）ＡＳＡ，ＡＥＳ及汽车用工程塑料ＰＣ／ＡＥＳ，ＰＢＴ／ＡＢＳ，ＰＣ／ＡＢＳ，ＰＡ／ＡＢＳ等合金材料欢迎来电或网上咨询