产品详细说明:
产品参数| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃5kg | ASTM D-1238 | 0.6 | g/10min |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | |
| 燃烧率 | File No. E56070 ULC-UL | 1/16HB | ||
| 熔体流动速率 | 220℃10kg | ASTM D-1238 | 6 | g/10min |
| 弯曲强度 | ASTM D-790 | 9070 | lb/in2 | |
| 弯曲强度 | ASTM D-790 | 640 | kg/cm2 | |
| 弯曲弹性率 | ASTM D-790 | 3.2105 | lb/in2 | |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 40 | kg.cm/cm |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 45 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 102 | R | |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 7.4 | ft.lb/in |
| 引张强度 | ASTM D-638 | 400 | kg/cm2 | |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 8.4 | ft.lb/in |
| 伸长率 | ASTM D-638 | 40 | % | |
| 引张强度 | ASTM D-638 | 5670 | lb/in2 | |
| 弯曲弹性率 | ASTM D-790 | 2.3104 | kg/cm2 | |
| 维卡软化点 | ASTM D-1525 | 105 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 221 | ℉ | |
| 热变形温度 | ASTM D-648 | 88(190) | ℉ | |
| 热变形温度 | ASTM D-648 | 98(208) | ℃ |
温馨提示：因市场价格变动较大，产品价格、图片仅供参考，具体请联系我们，谢谢！！
ABS性能:塑料ABS无毒、无味，外观呈象牙色半透明，或透明颗粒或粉状。密度为1.05~1.18g/㎝3，收缩率为0.4%~0.9%，弹性模量值为0.2Gpa，泊松比值为0.394，吸湿性250℃。力学性能:塑料ABS有优良的力学性能，其冲击强度极好，可以在极低的温度下使用；塑料ABS的耐磨性优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的耐蠕变性比PSF及PC大，但比PA及POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。热学性能:塑料ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一定的韧性，可在-40~100℃的温度范围内使用。电学性能:塑料ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。环境性能:塑料ABS不受水、无机盐、碱及多种酸的影响，但可溶于酮类、醛类及氯代烃中，受冰乙酸、植物油等侵蚀会产生应力开裂。ABS的耐候性差，在紫外光的作用下易产生降解；于户外半年后，冲击强度下降一半。