CY【值得信赖】生产氯化锌法煤质柱状活性炭/活性炭/木质粉状炭信息

产品详细说明:

CY【值得信赖】生产氯化锌法煤质柱状活性炭/活性炭/木质粉状炭

外观：黑色颗粒状.粉状 柱状 球状 颗粒装HF优质椰壳黄金炭 柱状椰壳活性炭 粉状椰壳活性炭 椰壳活性炭 性能：产品选用优质椰子壳为原料，具有比表面积大，强度高，吸附性能高等优点，产品规格齐全，有不规则破碎和小颗粒等几个大类。 用途：目前椰子壳活性炭是用于饮用水的净化、除氯、除藻、吸氧、催化载体方面效果最好的一种活性炭，可用于净水器、虑芯填充物等净水设备；可用于碳浆法，堆浸法和黄金提取以及冶金工业中贵金属的分离和提取，也可用于水质净化。 注意事项：1、活性炭在运输过程中，防止与坚硬物质混状，不可踩、踏，以防炭粒破碎，影响质量。2、储存应储存于多孔型吸附剂，所以在运输储存和使用过程中，都要绝对防止水浸，因水浸后，大量水充满活性空隙，使其失去作用。3、防止焦油类物质在使用过程中，应禁止焦油类物质带入活性炭床，以免堵塞活性炭空隙，使其失去吸附作用。最好有除焦设备净化气体。4、防火 活性炭在储存或运输时，防止与火源直接接触，以防着火、活性炭再生时避免进氧并再生彻底，再生后必须用蒸汽冷却降至80℃以下，否则温度高，遇氧，活性炭自燃。
分析项目	测试数据	分析项目	测试数据
碘值	>800mg/g	强度	>92％
比表面积	>850m2/g	亚甲兰值	120-150mg/g
总孔容积	>0.8cm3/g	余氯吸附率	≥85％
充填密度	0.45-0.55g/cm3
表中粒径分为1.0，1.5，2.0，3.0，4.0。其它指标可随用户需求调节

项目	指标
粒度	6-50目 任选
碘吸附值mg/g	850-1050
强度℅	≥90
干燥减度℅	≤10
灰份%	≤10
水份%	≤8
PH值	4.5-8
充填比重g/cm3	0.37-0.43

Activated carbon activated carbon activated carbon activated carbon activated carbon activated carbon activated carbon activated carbon coal granular activated carbonAppearance: black granularPerformance: Best high coconut shell as raw material, with large surface area, high intensity, high adsorption performance advantages, product specifications, with irregular fragmentation and small particles, and several other categories.Uses: coconut shell activated carbon is currently used for drinking water purification, dechlorination, algae, oxygen, catalytic effect of the best aspects of a carrier of activated carbon, can be used for water purification, consider water purification equipment such as core filler; available in carbon paste method, heap leaching and gold extraction and separation of the metallurgical industry and extraction of precious metals can also be used for water purification.Note:1,activated carbon during transport to prevent mixing with the hard physical shape, can not tread, to prevent carbon particles broken, affecting the quality.2,storage should be stored in the porous adsorbent, so the transport storage and use of the process, should absolutely prevent flooding, due to flooding, a large number of water full of activity in the gap, so useless.3,to prevent the tar substances during use should be prohibited tar substances into the activated carbon bed, so as nottoplugthegapactivated carbon, adsorption to lose. Better to havethancokegaspurificatioequipment.4,fire in the storage or transport when activated, to prevent direct contact with fire,Against fire, carbon into oxygen and recycled to avoid complete regeneration, regeneration must be cooled down to below 80℃steam, or high temperature case of oxygen, carbon ignition.SpecificationsProjectIndex

Granularity6-50 Head Optional

Iodine adsorption mg / g850-1050

Strength ℅≥ 90

Drying by degrees ℅≤ 10

Ash%≤ 10

Moisture%≤ 8

PH value4.5-8

Filling weight g/cm30.37-0.43